PA66 50%GF HB级适用于工业产品结构件领域，要求高强度、高韧性、耐高低温，常用作水阀分流器、出风口叶片、机械齿轮、衬套等。
物理性能
Ash | (50.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1538Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.1-0.3 % 1 ISO294-4) |
Shrinkage Vertical Flow | 0.2-0.5% I ISO294-4) |
机械性能
Tensile strength (217.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (17.0KJ/m2 I ISO179 Conditioned | 1.0J |
Flexural Strength (354 MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (14263 MPa I ISO178) Conditioned | 2mm/ min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (260*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 290-310°C |
Nozzle Temperature | 290-310*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整