PA66 20%玻璃纤维和无卤阻燃混合改性级非常受高要求阻燃结构件行业的欢迎，满足注塑级、增强级和阻燃级的特点；
无卤阻燃剂的优点是燃烧时烟度小，不会产生腐蚀性和有毒气体。
物理性能
Ash | (20.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1490Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.4-0.6 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.8-1.2% I ISO294-4) |
机械性能
Tensile strength (148.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.6% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (8.8KJ/m2 I ISO179) Conditioned | 1.0J |
Flexural Strength (227MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (7129 MPa I ISO178) Conditioned | 2mm/ min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (240*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | 1.6mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整