PA66 GF20热稳定型聚酰胺66是由20%的玻璃纤维混合而成的增强型聚酰胺66，可制成不同颜色，具有优异的耐高温综合性能。
PA66 20%玻璃纤维和热稳定混合改性等级非常受机械零件、离合器支架和；电气设备，具有耐热性和高机械强度。
物理性能
Ash | (20.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1280Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.5-0.9 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.8-1.1% I ISO294-4) |
机械性能
Tensile strength (142.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (7.8KJ/m2 IISO179) Conditioned | 1.0J |
Flexural Strength (234MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (6869 MPa I ISO178) Conditioned | 2mm/min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (245*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整