PA66 GF30是一种用30%玻璃纤维增强的聚酰胺66。它具有高流动性、高韧性、耐高温、易成型等优异的力学性能。
30%增强尼龙66的机械强度、抗蠕变性和疲劳强度显著提高，伸长率、模具收缩率、吸湿性和耐磨性降低。它可以是注塑成型塑料零件与应力结构领域的汽车，电子和机械；E、 家用电器和机械工业。
物理性能
Ash | (30.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1365Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.2-0.5 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.6-0.9% I ISO294-4) |
机械性能
Tensile strength (186.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.4% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (12.5 KJ/m2 IISO179) Conditioned | 1.0J |
Flexural Strength (282MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (8518 MPa I ISO178) Conditioned | 2mm/ min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (250*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整