PA66 45%GF HB级适用于齿轮领域，要求高强度、高韧性和动平衡，适用于运动器材和电动工具领域，要求高韧性、耐低温、低成本。通常用作机械外壳。
物理性能
| Ash | (45.0% 1 ISO3451/1) |
| Conditioned | 600°C*2h |
| Density | (1495Kg/m3 1 ISO1183) |
| Conditioned | 23°C |
| Shrinkage Parallel Flow | (0.1-0.3% 1 ISO294-4) |
| Shrinkage Vertical Flow | (0.4-0.6% I ISO294-4) |
机械性能
Tensile strength (204.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.8% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (16.5 KJ/m2 IISO179) Conditioned | 1.0J |
Flexural Strength (332MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (13547 MPa I ISO178) Conditioned | 2mm/min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (258*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 290-310°C |
Nozzle Temperature | 290-310*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整