PA66 20%玻璃纤维和卤化阻燃混合改性级非常受高要求阻燃结构件行业的欢迎，满足注塑级、增强级和阻燃级的特点；
卤代阻燃剂的优点是价格低、稳定性好、添加剂少、与合成树脂材料相容性好。
物理性能
Ash | (20.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1530Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.4-0.6 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.8-1.2% I ISO294-4) |
机械性能
Tensile strength (145.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (8.5KJ/m2 I ISO179) Conditioned | 1.0J |
Flexural Strength (225MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (7750 MPa I ISO178) Conditioned | 2mm/ min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (245*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | 1.6mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整