含15%玻璃纤维钢化塑料的PA6，由于其优异的性能、良好的外观和易于加工的特点，已成功应用于开关、控制器等电气领域，以及散热屏障、蓄能器外壳、冷却液罐、，电钻、电机外壳、泵叶轮、皮带轮、工具手柄、轴承等机械领域。
物理性能
Ash | (15.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1180Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.5-0.7 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.7-1.1% I ISO294-4) |
机械性能
Tensile strength (115.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.0% I ISO527) Conditioned | 1.0J |
Notched Impact Strength (125 0MPa I ISO527) Conditioned | 2mm/min |
Flexural Strength (175MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (5250 MPa I ISO178) Conditioned | 5mm/ min |
热性能
Melting Point | (220°C I ISO11357) |
Hot Deformation Temperature | (175*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 240-260°C |
Nozzle Temperature | 240-260*C |
Tooling Temperature | 80*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整