PA66 15%玻璃纤维和热稳定改性牌号应用于断路器、电气箱外壳、水泵外壳和盖等部门，具有高刚性和耐热变形性。
物理性能
Ash | (15.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1240Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.7-1.0 % 1 ISO294-4) |
Shrinkage Vertical Flow | (1.0-1.4% I ISO294-4) |
机械性能
Tensile strength (108.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.2% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (5.5KJ/m2I ISO179) Conditioned | 1.0J |
Flexural Strength (190MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (5400MPa I ISO178) Conditioned | 2mm/ min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (240*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整