PA66 15%玻璃纤维和卤素阻燃改性等级适用于电气、电子和电力行业的阻燃结构部件，具有低成本、高外观和易于成型的特点。是电动工具割草机机壳原材料的良好选择。
物理性能
Ash | (15.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1450Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.4-0.6 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.8-1.2% I ISO294-4) |
机械性能
Tensile strength (130.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.3% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (6.5KJ/m2 I ISO179) Conditioned | 1.0J |
Flexural Strength (200MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (6500MPa I ISO178) Conditioned | 2mm/min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (240*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | 1.6mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整