安美工程师在30%玻璃填充尼龙66中添加了一定量的橡胶或弹性体，使其冲击强度加倍。增韧弹性体可有效提高尼龙的抗冲击性和低温性能。
PA66 GF30增韧广泛应用于工业产品齿轮结构件，以及电机齿轮、电动阀门等日用品结构件。
物理性能
Ash | (30.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1300Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.2-0.5 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.6-0.9% I ISO294-4) |
机械性能
Tensile strength (164.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (3.5% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (15.8KJ/m2 IISO179) Conditioned | 1.0J |
Flexural Strength (255MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (8169 MPa I ISO178) Conditioned | 2mm/ min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (240*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整