卤代阻燃剂的优点是能保持阻燃产品原有的物理化学性能。
物理性能
Ash | (30.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1590Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.2-0.5 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.6-0.9% I ISO294-4) |
机械性能
Tensile strength (155.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.7% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (8.5 KJ/m2I ISO527) Conditioned | 1.0J |
Flexural Strength (240MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (10258 MPa I ISO178) Conditioned | 2mm/ min |
热性能
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (245*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | 1.6mm |
注射成型条件
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整