PA66 GF20(A2000D)

用20%的玻璃纤维在基体PA66上增强,称为PA66 GF20,它提高了注塑成型的尺寸稳定性和抗冲击性。

PA66 GF20(A2000D)的典型应用

由于其高刚度、尺寸稳定性、噪音降低、耐磨性、静音、润滑性和抗静电性,适用于各种精密齿轮。

PA66 GF20(A2000D)的加工详图

PA66 GF20(A2000D)的加工详图

PA66 GF20(A2000D)的其他详细信息

物理性能

Ash

(20.0% 1 ISO3451/1)

Conditioned

600°C*2h

Density

(1285Kg/m3 1 ISO1183)

Conditioned

23°C

Shrinkage Parallel Flow

(0.5-0.9 % 1 ISO294-4)

Shrinkage Vertical Flow

(0.8-1.1% I ISO294-4)

机械性能

Tensile strength (145.0MPa 1 ISO527)

Conditioned

5mm/ min

Tensile Strain at Break (2.5% I ISO527)

Conditioned

5mm/min

Notched Impact Strength (8.5KJ/m2 I ISO179)

Conditioned

1.0J

Flexural Strength (235MPa 1ISO178)

Conditioned

2mm/min

Flexural Modulus (6876 MPa I ISO178)

Conditioned

2mm/ min

热性能

Melting Point

(260°C I ISO11357)

Hot Deformation Temperature

(245*C I ISO75)

Conditioned

1.8MPa

Flammability Class

(HB 1UL94)

Conditioned

mm

注射成型条件

Drying Temperature

130°C

Drying Time

3h

Cylinder Temperature

280-300°C

Nozzle Temperature

280-300*C

Tooling Temperature

80-100*C

*成型条件为;只是;仅供参考,请根据实际情况进行调整