20%弹性体增韧尼龙66用于注塑成型。可用于制备齿轮、衬套、滑块、活塞等零件，具有良好的耐磨性。
物理性能
Ash | (15.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1104Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (1.3-1.6 % 1 ISO294-4) |
Shrinkage Vertical Flow | (1.3-1.6% I ISO294-4) |
机械性能
Tensile strength (60.0MPa 1 ISO527) Conditioned | 50mm/min |
Tensile Strain at Break (39.0% I ISO527) Conditioned | 50mm/min |
Notched Impact Strength (28.6 KJ/m2 IISO179) Conditioned | 2.75J |
Flexural Strength (80MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (1960MPa I ISO178) Conditioned | 2mm/ min |
热性能
Melting Point | (220°C I ISO11357) |
Hot Deformation Temperature | (160*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
注射成型条件
Drying Temperature | 90°C |
Drying Time | 3h |
Cylinder Temperature | 255-275°C |
Nozzle Temperature | 255-275*C |
Tooling Temperature | 80*C |
*成型条件为；只是；仅供参考，请根据实际情况进行调整